高强度, 良好的抗热老化性, 抗溶解性, 热稳定性, 脱模性能良好, 高温应用

Radici Compounds N66N50HSL

聚酰胺66

Radici Plastics USA, Inc.

Technical Data

 

产品说明

 

These formulations are nylon 6.6 compounds, nucleated to accelerate crystallization and incorporating an especially effective mold release.

 

For molded parts, which may be exposed to high temperatures for prolonged periods of time, one of the heat stabilized grades should be selected. N6650HSL contains a conventional stabilizer system, which provides excellent protection against thermal aging, but can slightly tint the natural color, normally to a greenish hue. For applications where preservation of natural color is important, especially for precision color matches, the use of N6650HL, which incorporates an effective stabilizer system free from color effects, is recommended. The properties of these heat-stabilized grades are similar to those of the general-purpose product, with the exception of elongation to break, which may be slightly reduced.

 

These formulations are recommended for applications where very short cycle times are required, especially for high production multi-cavity tools. Compared with a general-purpose product such as N6650L, these nucleated grades exhibit higher strength and rigidity, but lower practical toughness. Mold shrinkage is also lower, and less anisotropic, often resulting in reduced tendency for warpage.

 

Nylon 6.6 offers a unique combination of strength and toughness, excellent static and dynamic fatigue resistance, natural lubricity and resistance to the effects of a broad range of chemicals, oils and solvents, and is therefore used for a very wide range of applications in every end-use category.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing - MDE PA66 (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Radici Plastics USA, Inc.

供货地区 • 北美洲

添加剂 • 成核剂 • 热稳定剂 • 润滑剂

• 刚性，高 • 良好的抗热老化性 • 生产阶段，快

• 高强度 • 耐化学性良好

性能特点 • 脱模性能良好

• 经润滑 • 耐油性能

• 有核

• 抗溶解性 • 热稳定性

用途 • 高温应用

外观 • 可用颜色 • 自然色

形式 • 颗粒料

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.14g/cm³ ASTM D792

收缩率 - 流动 (3.18 mm) 1.0 到 1.4% ASTM D955

吸水率 (24 hr) 1.2% ASTM D570

机械性能 额定值单位制 测试方法

抗张强度 (断裂) 96.5MPa ASTM D638

伸长率 (断裂) 15 到 25% ASTM D638

弯曲模量 3030 到 3170MPa ASTM D790

弯曲强度 (屈服) 128MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (23°C, 3.18 mm) 43 到 48J/m ASTM D256

拉伸冲击强度 3 (23°C) 315kJ/m² ASTM D1822

硬度 额定值单位制 测试方法

洛氏硬度 (R 计秤) 123 ASTM D785

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 90.0°C ASTM D648

熔融温度 250 到 265°C ASTM D789

注射 额定值单位制

干燥温度 82.2°C

干燥时间 4.0hr

 

Radici Compounds N66N50HSL

聚酰胺66

Radici Plastics USA, Inc.

注射 额定值单位制

建议的最大水分含量 0.25%

螺筒后部温度 282°C

螺筒中部温度 279°C

螺筒前部温度 277°C

加工（熔体）温度 271 到 293°C

模具温度 60.0 到 82.2°C

背压 0.345MPa

螺杆转速 40 到 80rpm

垫层 3.18 到 6.35mm

 

 

 

 

 